射出磁石膠粒－Ｎd-
Fe-B
| 項目
|
測定法 |
單位 |
等方性 |
異方性 |
| 12尼龍 |
12尼龍 |
12尼龍 |
PPS |
12尼龍 |
| RNI-1255S |
RNI-1260S |
RNI-1265S |
RNI-1655 |
RNI-5211 |
| 密度 |
ASTM D792 |
g/cm² |
5.0~5.2 |
5.1~5.3 |
5.3~5.5 |
5.1 |
4.9 |
| 強度 |
ASTM
D790 |
N/m²(108)
|
>0.8 |
0.7 |
0.9 |
| Kg/cm² |
>800 |
700 |
980 |
| 曲彈性率 |
ASTM
D790 |
N/m²(1010) |
>1.08 |
2.10 |
1.13 |
| Kg/cm²(105) |
>1.10 |
2.14 |
1.15 |
| IZOD衝擊強度 |
ASTM
D256 |
J/m |
>9800 |
7800 |
13700 |
| khfcm/cm |
>10 |
8 |
14 |
| 流動性270C/10kg |
ASTM
D1238 |
g/10min |
>215 |
>100 |
>75 |
*50 |
70 |
| 熱變形溫度 |
ASTM
D648
(18.5kg/cm) |
°C |
145 |
150 |
150 |
200 |
145 |
| 成形收縮率 |
金型溫度 射出壓力
80C1,400kg/cm |
% |
0.42 |
0.40 |
0.40 |
0.25 |
0.80 |
| 磁氣特性 |
Br |
T |
0.52~0.55 |
0.54~0.56 |
0.57~0.60 |
0.53 |
0.70 |
| G |
5200~5500 |
5400~5600 |
5700~6000 |
5300 |
7000 |
| iHc |
KA/m |
>=560 |
710 |
1060 |
| Oe |
>=7000 |
9000 |
13400 |
| bHc |
KA/m |
320~370 |
320~370 |
350~390 |
350 |
510 |
| Oe |
4000~4600 |
4100~4700 |
4400~5000 |
4400 |
6400 |
| BHmax |
Kj/m3 |
44~52 |
48~56 |
54~62 |
49 |
95 |
| MGOe |
5.5~6.5 |
6.0~7.0 |
6.8~7.8 |
6.1 |
11.9 |
| 可逆溫度變化 |
-Br/Br/-T(%0C) |
-0.105 |
-0.09 |
| -iHC/iHC/-T(%/0C) |
-0.400 |
-0.55 |
|
|
|
|
|